Filimu Yokutidwa ndi Aluminiyamu ya BOPP Yopingasa Kwambiri
Chiyambi cha Zamalonda:
Filimuyi ili ndi kumatirira kwabwino kwambiri kwa aluminiyamu, komwe kumawonjezera mphamvu ya zinthu zina. Yapangidwa kuti igwiritsidwe ntchito ngati gawo lapakati m'mapangidwe a magawo atatu, zomwe zimapangitsa kuti zinthu zikhale zofanana. Filimuyi imapereka mphamvu zabwino kwambiri zotchingira mpweya ndi chinyezi, zomwe zimapangitsa kuti nthawi yosungiramo zinthu ikhale yotalika.
Mapulogalamu Ogwiritsira Ntchito:
Ndi kuwala kwachitsulo, imaletsa kuwala kooneka ndi kuwala kwa ultraviolet, zomwe zimapangitsa kuti zinthu zomwe zapakidwa m'matumba zisamawonongeke. Filimuyi imaperekanso ntchito yabwino yokonza zinthu komanso yobwezeretsa chilengedwe. Imagwiritsidwa ntchito kwambiri popaka zipatso zouma, tiyi, chakudya chopanda madzi, mankhwala, ndi zina zambiri.
Kapangidwe ka Njira:
BOPP / Chithandizo cha Malo Ophimbidwa (Mzere wa Mbeu za Alubond kapena Chophimba) / Mzere wa Aluminiyamu
Mafotokozedwe:
- Kukhuthala kwa Zinthu Zoyambira: 12–50 μm
- M'lifupi ndi Miyeso: Yosinthika kutengera zomwe makasitomala akufuna.
Katundu Wamba:
| Chinthu Choyesera | Njira Yoyesera | Chigawo | VMOPP-GZ010 | VMOPP-GZ110 | VMOPP-GZ111 |
| Makulidwe a Zinthu Zoyambira | GB/T 6672 | μm | 18 | 18 | 18 |
| Kukhuthala kwa Aluminiyamu | GB/T 15717 | ZA | ≥2.2 | ≥2.4 | ≥2.4 |
| Kumatira kwa Aluminiyamu | Njira Yoyesera ya EAA | N/15mm | ≥2.0 | ≥3.0 | ≥3.0 |
| Kunyowetsa (Pamwamba Pokutidwa ndi Aluminiyamu) | GB/T 14216 | mN/m | ≥40 | ≥40 | ≥40 |
| Kunyowetsa (Pamwamba Popanda Aluminiyamu) | GB/T 14216 | mN/m | ≥36 | ≥36 | ≥36 |
| Mphamvu Yokoka (MD) | GB/T 1040.3 | MPa | ≥120 | ≥120 | ≥120 |
| Mphamvu Yokoka (TD) | GB/T 1040.3 | MPa | ≥200 | ≥200 | ≥200 |
| Kutalika pa Break (MD) | GB/T 1040.3 | % | ≤180 | ≤180 | ≤180 |
| Kutalika pa Kupuma (TD) | GB/T 1040.3 | % | ≤65 | ≤65 | ≤65 |
| Kutumiza kwa Nthunzi ya Madzi (WVTR) | ASTM F-1249 | g/(m²·24h) | ≤1.0 | ≤0.8 | ≤0.5 |
| Kuchuluka kwa Mpweya wa Oxygen (OTR) | ASTM D-3985 | cm³/(m²·24h·0.1MPa) | ≤1.0 | ≤0.5 | ≤0.3 |